In this dissertation, we studied the barocaloric effect with spin-crossover transition in the compound CrI₂(depe)₂. We obtained an giant isothermal entropy change (∆Sꚍ) and an adiabatic temperature change (∆Tad) under a moderate pressure variation applied on the system. The compound was investigated considering three contributions to entropy: configurational, magnetic and phonons, which were simulated using specific microscopic parameters. The high values of ∆Sꚍ = 40 J.kg⁻¹ .K⁻¹ e ∆Tad = 10.6 K for a ∆P = 2.0 kbar were obtained around the (T½) phase transition temperature between low ↔ high spin, and qualify it as a material with a giant barocaloric effect. In addition, due to the high value of the barocaloric parameter (δT½/δP approx52 K/kbar), a giant cooling capacity (RC = 3583 J.kg⁻¹) was determined for the compound CrI₂(depe)₂.
Nesta dissertação, estudamos o efeito barocalórico com transição do tipo spin-crossover no composto CrI₂(depe)₂. Obtivemos uma variação isotérmica da entropia (∆Sꚍ) gigante e uma variação adiabática da temperatura (∆Tad) sob uma variação de pressão moderada aplicada sobre o sistema. O composto foi investigado considerando três contribuições para a entropia: configuracional, magnética e da rede cristalina, que foram simuladas utilizando parâmetros microscópicos próprios. Os altos valores de ∆Sꚍ = 40 J.kg⁻¹ .K⁻¹ and ∆Tad = 10.6 K para um ∆P = 2.0 kbar foram obtidos em torno da temperatura (T½) de transição de fase entre low ↔ high spin, e o qualificam como um material com efeito barocalórico gigante. Além disso, devido ao alto valor do parâmetro barocalórico (δT½/δP ≈ 52 K/kbar), uma gigante capacidade de refrigeração (RC = 3583 J.kg⁻¹) foi determinada para o composto CrI₂(depe)₂.