In this dissertation we present the synthesis and investigation of ceramic samples Mg2SnO4 doped with 0.1% of Co2+ ions. The samples were synthesized by solid state reaction through the stoichiometry of the ultrapure reagents MgO, SnO2 and CoCO3. The phases formed in the samples were identified by X-ray diffraction. The optical characterization of the samples was performed by photoluminescence at room temperature and atmospheric pressure. From the emission and excitation spectra and the decay time measurements, the fundamental and excited states of the impurity ion Co2+ were identified and the parameters of crystalline field, Dq, and Racah, B and C were determined.
Nessa dissertação apresentamos a síntese e a investigação de amostras cerâmicas Mg2SnO4 dopadas com 0,1% de íons Co2+. As amostras foram sintetizadas por reação do estado sólido entre os reagentes ultrapuros MgO, SnO2 e CoCO3. As fases formadas nas amostras foram identificadas através da Difração de Raios X. A caracterização óptica das amostras foi realizada através da fotoluminescência à temperatura ambiente e pressão atmosférica. A partir dos espectros de emissão, excitação e das medidas de tempo de decaimento, foram identificados os estados fundamental e excitados do íon impureza Co2+ e determinados os parâmetros de Campo Cristalino, Dq, e de Racah, B e C.